• WUXI XINFUTIAN METAL PRODUCTS CO., LTD
    Sam-USA
    Vey good BA and HL Finish ,and the same time good package to protect the goods
  • WUXI XINFUTIAN METAL PRODUCTS CO., LTD
    Fathiha-UAE
    Fast delivery time,good quality From WUXI XINFUTIAN METAL PRODUCTS CO.,LTD ,hope to have a win-win business in the future .
  • WUXI XINFUTIAN METAL PRODUCTS CO., LTD
    Abbas-Pakistan
    We Have Cooperation With this Factory Many Years , Everything Goes Very Well.l Like This Factory !
Contact Person : Amy
Phone Number : 13327910097

Thin 0.8mm Stainless Steel Sheet Coil Grade 444 For Hot Water Tanks

Place of Origin SHANGHAI
Brand Name BAOSTEEL,TISCO,JISCO ,LZ
Certification BV,SGS,ISO
Model Number 400 Series 444
Minimum Order Quantity 1 ton
Price Negotiation
Packaging Details Standard export seaworthy package or as customer required
Supply Ability 2000 ton/Month
Product Details
Name 444 Stainless Steel Plate Standard JIS/ASTM/AISI/GB
Width 1000.1219,1500 Length 2438.3048 As Customized
Type Cold Rolled Sheet Steel Edge Mill Edge
High Light

Thin 0.8mm Stainless Steel Sheet

,

Grade 444 Stainless Steel Sheet

,

Cold Rolled Stainless Sheet Mill Edge

Leave a Message
Product Description

Stainless Steel Sheet Or Coil Grade 444 For Hot-Water Tanks

 

Strip, Coil, Foil, Wire, ASTM A268, ASTM A240

APPLICATIONS

Food processing, brewery and wine making equipment, hot-water tanks, heat-exchanger tubing and automotive components

DESCRIPTION

Type 444 is a low carbon, low nitrogen, ferritic stainless steel that provides pitting and crevice corrosion resistance superior to most ferritic stainless steels. Applications requiring superior corrosion resistance and resistance to chloride stress corrosion cracking are ideal for this alloy.

CHEMISTRY TYPICAL

Carbon: 0.025 max
Manganese: 1.00 max
Silicon: 0.60
Chromium: 17.50-19.50
Nickel: 01.00 max
Molybdenum: 1. 75-2.50
Titanium+ Columbium : 0.20 + 4x (Carbon+ Nitrogen) min-0.80 max
Phosphorus: 0.040 max
Sulfur: 0.030 max
Iron: Balance

PHYSICAL PROPERTIES

Density: 0.28 lbs/in3 7.75 g/cm3

Electrical Resistivity: microhm-in (microhm-cm):
68 ° F (20 ° C): 22.50 (57)

Specific Heat: BTU/lbl° F (kJ/kg•K):
32 - 212 ° F (0 - 100 ° C): 0.102 (0.427)

Thermal Conductivity: BTU/hr/ft2/ft/° F (W/m•K)
At 212 °F (100 °C): 15.5 (26.8)

Mean Coefficient of Thermal Expansion: in/inl° F (µm/m•K):
32 - 212 ° F (0 - 100 °C): 6.1 x 10-s (11.0)

Modulus of Elasticity: ksi (MPa)
29 x 103 (200 x 103) in tension
 

Magnetic Permeability: Magnetic

Melting Range: 2700 - 2790 ° F (1482 - 1532 °C)

FORMS

Coil - Strip, Foil, Ribbon Wire - Profile, Round, Flat, Square

MECHANICAL PROPERTIES AT ROOM TEMPERATURE

PROPERTIES: ANNEALED

Ultimate Tensile Strength: 60 KSI min (414 MPa min)
Yield Strength (0.2% offset): 40 KSI min (276 MPa min)
Elongation: 22% min
Hardness: Rb 90 max

PROPERTIES: TEMPERED

Type 444 can be rolled to various tempers. Consult Ulbrich Technical Services if temper rolled product is required.

FINISHES

# 1 Hot rolled annealed and descaled. It is available in strip, foil and ribbon. It is used for applications where a smooth decorative finish is not required.
#2D Dull finish produced by cold rolling, annealing and descaling. Used for deep drawn parts and those parts that need to retain lubricants in the forming process. # 2B - Smooth finish produced by cold rolling, annealing and descaling. A light cold rolling pass is added after anneal with polished rolls giving it a brighter finish than 2D.
#BA Bright annealed cold rolled and bright annealed
#CBA Course bright annealed cold rolled matte finish and bright anneal
2BA Smooth finish produced by cold rolling and bright annealing. A light pass using highly polished rolls produces a glossy finish. A 2BA finish may be used for lightly formed applications where a glossy finish is desired in the formed part. Polished - Various grit finish for specific polish finished requirements.

Thin 0.8mm Stainless Steel Sheet Coil Grade 444 For Hot Water Tanks 0